CONSTANTES PHYSIQUES DES MÉTAUX
TEMPÉRATURES (°C) |
MASSE VOLUMIQUE (g.cm-3 ou kg.dm-3) |
COEFFICIENT DE DILATATION (en ppm / °C) |
CAPACITÉ CALORIF.MASSIQUE Csolide (J.kg-1.°C-1) |
|||
MÉTAL |
SYMBOLE |
FUSION |
ÉBULLITION |
|||
| ALUMINIUM | Al |
660 |
2447 |
2.7 |
25 |
899 |
| ANTIMOINE | Sb |
630 |
1750 |
6.6 |
9 |
209 |
| ARGENT | Ag |
962 |
2212 |
10.5 |
19 |
238 |
| BÉRYLLIUM | Be |
1978 |
2970 |
1.8 |
12 |
1824 |
| CADMIUM | Cd |
320 |
765 |
8.6 |
30 |
230 |
| CHROME | Cr |
1860 |
2670 |
7.2 |
6 |
480 |
| COBALT | Co |
1495 |
2870 |
8.7 |
12 |
418 |
| CUIVRE | Cu |
1083 |
2567 |
8.7 |
12 |
385 |
| ÉTAIN | Sn |
232 |
2270 |
7.3 |
20 |
226 |
| FER | Fe |
1535 |
2750 |
7.7 |
12 |
452 |
| IRIDIUM | Ir |
2410 |
4130 |
22.4 |
6 |
129 |
| MAGNÉSIUM | Mg |
649 |
1090 |
1.7 |
25 |
1017 |
| MANGANÈSE | Mn |
1244 |
1090 |
7.2 |
22 |
477 |
| MERCURE | Hg |
-39 |
1962 |
13.6 |
- |
138 |
| MOLYBDÈNE | Mo |
2617 |
4612 |
9.0 |
5 |
251 |
| NICKEL | Ni |
1453 |
2732 |
8.9 |
13 |
443 |
| OR | Au |
1064 |
2807 |
19.3 |
14 |
130 |
| OSMIUM | Os |
3045 |
5027 |
22.4 |
5 |
130 |
| PLATINE | Pt |
1772 |
3827 |
21.4 |
9 |
134 |
| PLOMB | Pb |
327 |
1740 |
11.4 |
29 |
130 |
| POTASSIUM | K |
63 |
774 |
0.8 |
83 |
753 |
| RHODIUM | Rh |
1966 |
3727 |
12.4 |
8 |
243 |
| SILICIUM | Si |
1410 |
1755 |
2.3 |
3 |
711 |
| TITANE | Ti |
1660 |
3287 |
4.5 |
9 |
523 |
| TUNGSTÈNE | W |
3410 |
5660 |
19.0 |
4.5 |
134 |
| VANADIUM | V |
1890 |
3380 |
6.0 |
8 |
485 |
| ZINC | Zn |
419 |
907 |
7.1 |
35 |
389 |
| ZIRCONIUM | Zr |
1852 |
4377 |
6.5 |
- |
- |
|
|
|